Effect of silica on the properties of elastomeric materials based on NR/BR/SBR ternary rubber blend
Датум постављања документа
2018-11-02Аутори
Jovanović, Slaviša
Jovanović, Vojislav
Marković, Gordana
Marinović-Cincović, Milena
Vukić, Nevena
Samaržija-Jovanović, Suzana
Budinski-Simendić, Jaroslava
Метаподаци
Приказ свих података о документуАпстракт
The effects of pyrogeneous silica on the mechanical properties of elastomeric materials based on natural rubber (NR), polybutadiene rubber (PB) and styrene-butadiene rubber (SBR) are reported. For sample preparations the content of network precursor was constant (25:25:50), but the content of filler was varied (0, 40, 60, 80, 100 phr). Curing behavior was assessed using oscillating disc rheometer. Results indicated that the minimum torque and maximum torque increase with increasing filler loading in the compounds, whereas scorch time shows a decreasing trend. Cure time of obtained composites increases with increasing filler loading. Mechanical properties were evaluated before and after thermal ageing (during 72h or 168h at 100oC) of obtained composite materials. Incorporation of silica has improved the tensile modulus. However, elongation at break exhibited a different trend. For tensile strength, optimum values were obtained at 60 phr silica content
М категорија
M33openAccess
M33
openAccess